| Stainless Steel Starp
|
Chemical composition
|
Symbol of grade |
C |
Si |
Mn |
P |
S |
Ni |
Cr |
Mo |
|
Max % |
|
SUS 304 |
0.080 |
1.000 |
2.000 |
0.045 |
0.030 |
8.0 to 20.0 |
18.00 to 20.0 |
- |
|
SUS 301 |
0.030 |
1.000 |
2.000 |
0.045 |
0.030 |
6.0 to 8.0 |
16.00 to 18.00 |
- |
|
SUS 316L |
0.030 |
0.750 |
2.000 |
0.045 |
0.030 |
10.0to14.0 |
16.00 to 18.00 |
2.00 to 3.00 |
|
SUS 430 |
0.120 |
0.750 |
1.000 |
0.040 |
0.030 |
- |
16.00 to 18.00 |
- |
|
SUS 410S |
0.080 |
1.000 |
1.000 |
0.040 |
0.030 |
- |
11.50 to 13.50 |
- |
|
SUS 202 |
0.150 |
1.000 |
10.00 |
0.060 |
0.030 |
4.0 to 6.0 |
17.00 to 19.00 |
- |
Hardness & Mechanical properties
|
Designation of grade |
Finish |
Hardness
(HV)-Max |
Yield Strength
(Kg/mm²)-Min |
Tensile Strengthg/mm²)-Min |
Elongation
(%)-Min |
|
SUS 304 |
BA |
200 |
20.50 |
52.00 |
40 |
|
SUS 316L |
BA |
200 |
17.50 |
48.00 |
40 |
|
SUS 430 |
BA |
200 |
20.50 |
45.00 |
22 |
|
SUS 410S |
BA |
200 |
20.50 |
41.00 |
20 |
|
SUS 202 |
BA |
218 |
24.50 |
59.00 |
40 |
Hardness & Mechanical properties
|
Designation of grade |
Symbol of temper |
Hardness
(HV)-Max |
Yield Strength
(Kg/mm²)-Min |
Tensile Strength(Kg/mm²)-Min |
Elongation
(%)-Min |
|
SUS 301 |
½H |
310 |
51.00 |
93.00 |
10 |
|
|
¾H |
370 |
74.50 |
113.00 |
5 |
|
|
H |
430 |
103.00 |
132.00 |
|
|
|
EH |
490 |
127.50 |
157.00 |
|
|
SUS 304 |
½H |
250 |
47.00 |
78.00 |
6 |
|
|
¾H |
310 |
66.50 |
93.00 |
3 |
|
|
H |
370 |
88.00 |
113.00 |
|
|
| |
|
|
|